"Study of Incipient Melting & Stress Rupture Properties in Iron-Base Superalloy A286 "
"The process for manufacturing iron-based superalloy A286 was investigated. To produce the premium superalloy A286, incipient melting and stress-rupture notch sensitivity must be completely controlled ...
Sila login untuk meminjam buku.
"Surface Quality Improvement of High Carbon Steel Slab for Twin Slab Casting "
"In the solidification process of high carbon steel with carbon contents in the range of 0.45-1.0 mass%, wide temperature range of austenite single-phase leads to coarse grains. In addition, high carb ...
Sila login untuk meminjam buku.
"Technology Development for Reducing Scale Defect on Surface of H-Beam "
" Scale defects are one of critical problems at hot steel rolling process Scale is formed during heating and cooling of rolling process Generally, conditions of reheating furnace and cool ...
Sila login untuk meminjam buku.
"The Effect of Precipitates Control & Grain Boundary Strengthening in Ultra-Low Carbon Steels "
"Ultra-low carbon (ULC) steels are well-known for superior formability but relatively low strength due to a lack of strong solid solution hardening by carbon solutes. The common strengthening mechanis ...
Sila login untuk meminjam buku.
"The Effects of Niobium & Molybdenum Additions on Bending Property of Hot Stamping Steels "
"In order to improve the bending property of higher strength grade hot stamping steel, the traditional manganese-boron steel should be modified by an adjustment of alloy elements, such as niobium, mol ...
Sila login untuk meminjam buku.
"The Human Factor at BSW – Efficiency by Motivation, Qualification and Flexibility!"
"Currently, the steel industry is in a tough situation. BSW, like each and every steelmaker around the world, faces the challenge to compete successfully in the long-term in this difficult busines ...
Sila login untuk meminjam buku.
"The Improvement in the Central Porosity of Billets at the EAF Plant of Dragon Steel Corporation "
"The billets are produced at high casting speed due to the small cross-section at Dragon Steel Corporation (DSC). However, the high casting speed makes the central porosity defects more serious. The t ...
Sila login untuk meminjam buku.