South East Asia Iron and Steel Institute
Improvement of Surface Quality and Castability of Al-TRIP Steel
by Yuichi Oka, Takashi Miyake
High aluminum steel changes mold flux composition significantly more than conventional steel grades because of the reaction between the aluminum in the molten steel and SiO2 in mold flux during contin ...
Read More
Please login to borrow the book.
Improvement of Wire Rods Processing Technology
by Hideyuki Ohshima, Toshifumi Idesako
Godo Steel, Ltd. Osaka Works started at the place of current Osaka Works in 1937. Wire rods Mill was established in 1982 and main specification of rolling equipment is the mill of the 2 strands and fi ...
Read More
Please login to borrow the book.
Improvement of Zinc Dross Formation during Hot-Dip Galvanizing Process
by Yu-Ming Chang, Tien-Yu Hsieh
Improvement of Zinc Dross Formation during Hot-Dip Galvanizing Process
Read More
Please login to borrow the book.
Improvement on Corner Crack Defect for Plate Products Making From Slabs
by Ching Chang Lin
The corner crack of the plate is mainly caused by the corner transversal cracks and longitudinal corner cracks of slab, which need to cut the slab corner or hand scarf the slab corner before it is dis ...
Read More
Please login to borrow the book.
Improving Environmental & Life Of Tundish Working Lining In Continuos Casting Area
by Ngo Tien Tho
Reduce consumption of refractory (30% or 0.5 kg/T means 0.25 €/T):
Saving:125.000 €/year
Reduce manpower for repairing
Reduce gas consumption for drying
Saving: 3.468 mmBTU ...
Read More
Please login to borrow the book.
Improving Pre-Heating Process in No.3 RCM Furnace of CSC
by Lai Cheng-Long
3RCM is so called reversing cold rolling mill and dedicated to producing high-grade electrical steel (ES). High ductile-to-brittle transition temperature of high silicon content ES is apt to suffer br ...
Read More
Please login to borrow the book.
Improving Safety Performance by Collaborative Workplace Hazards Finding
by Lee Tzu-yu, Tong Pao-Hong
Iron and steel industry is one of the high risk heavy industry, using heavy-duty machines and equipments for production and movement of large masses of materials, that generate health and safety hazar ...
Read More
Please login to borrow the book.
Improving the Edge Waves Phenomenon of Cold-Rolled Thin Strips in the Skin-Pass Mill of Continuous Annealing Line
by Chia-Ching Lin, Jui-Sheng Weng
SECC grade sheets can be used for LCD back-plates. Because there has been a trend for cold-rolled strips toward thinner, therefore how to prevent the occurrences of edge waves during cold rolling is o ...
Read More
Please login to borrow the book.